PC+PET Infino AE-2130 LOTTE KOREA

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.23 g/cm³
density	density		ISO 1183	1.23 g/cm³
melt mass-flow rate	250°C/2.16kg	ASTM D1238	2.8 g/10min
	melt mass-flow rate	260°C/5.0kg	ASTM D1238	21 g/10min
		melt mass-flow rate	250°C/2.16kg	ISO 1133	2.8 g/10min
		melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ISO 1133	21 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30to0.50 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.30to0.50 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.30to0.50 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.30to0.50 %
ash content	--	ISO 3451	4.0 %
ash content	ash content	--	ASTM D5630	4.0 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	111
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	111

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ISO 180/1A	38 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	33 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	550 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	180 J/m

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength		ASTM D790	81.0 MPa
bending strength	bending strength		ISO 178	82.0 MPa
Tensile modulus		ASTM D638	2300 MPa
Tensile modulus	Tensile modulus		ISO 527-2/50	2400 MPa
tensile strength	Yield	ASTM D638	57.0 MPa
	tensile strength	Yield	ISO 527-2/50	56.0 MPa
		tensile strength	Break	ASTM D638	56.0 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0 MPa
elongation	Break	ASTM D638	90 %
Tensile strain	Break	ISO 527-2/50	90 %
Flexural modulus		ASTM D790	2500 MPa
Flexural modulus	Flexural modulus		ISO 178	2400 MPa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	128 °C
	Heat distortion temperature	0.45MPa,Unannealed,4.00mm，HDT	ISO 75-2/B	120 °C
		Heat distortion temperature	0.45MPa,Annealed,4.00mm，HDT	ISO 75-2/B	125 °C
			Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	108 °C
				Heat distortion temperature	1.8MPa,Unannealed,4.00mm，HDT	ISO 75-2/A	98.0 °C
				Heat distortion temperature	Heat distortion temperature	1.8MPa,Annealed,4.00mm，HDT	ISO 75-2/A	112 °C
vicat		ISO 306/B50	132 °C