EHMWPE Plaslube® PE 4000 LE Techmer Polymer Modifiers
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| density | ASTM D792 | 0.941 g/cm³ | |
| melt mass-flow rate | 190°C/1.05kg | ASTM D1238 | 4.0 g/10min |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 2.2 % |
| Water absorption rate | 24hr | ASTM D570 | 0.070 % |
| tensile strength | Break | ASTM D638 | 32.4 MPa |
| elongation | Break | ASTM D638 | 80 % |
| Flexural modulus | ASTM D790 | 896 MPa | |
| bending strength | ASTM D790 | 48.3 MPa | |
| coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.27 |
| limiting pv value | 100fpm | ASTM D3702 | 5000 psi·fpm |
| 1000fpm | ASTM D3702 | 2500 psi·fpm | |
| coefficient of friction | 与钢-静态6 | ASTM D1894 | 0.19 |
| 磨损因数 | ASTM D1894 | 120 10^-8mm³/N·m | |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | NoBreak |
| Rockwell hardness | R-Scale | ASTM D785 | 66 |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 93.3 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 54.4 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9.5E-05 cm/cm/°C |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| limiting pv value | 10fpm | ASTM D3702 | 3000 psi·fpm |