PA66 Vydyne® 47H BK0644
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 1.6 % |
| MD:23°C,2.00mm | ISO 294-4 | 1.8 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| 平衡,23°C,50%RH | ISO 62 | 2.3 % | |
| Outdoor applicability | UL 746C | f1 | |
| density | ISO 1183 | 1.10 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 725 °C |
| 1.5mm | IEC 60695-2-13 | 800 °C | |
| 3.0mm | IEC 60695-2-13 | 725 °C | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 700 °C |
| 1.5mm | IEC 60695-2-12 | 775 °C | |
| 3.0mm | IEC 60695-2-12 | 700 °C | |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 3.0mm | UL 94 | HB |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Automotive Materials | thicknessd=1mm | FMVSS302 | + |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ISO 180 | 12 kJ/m² |
| -30°C | ISO 180 | 16 kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 11 kJ/m² |
| -30°C | ISO 179/1eA | 17 kJ/m² | |
| 23°C | ISO 179/1eA | 19 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 18 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 2780 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 60.0 MPa |
| bending strength | 23°C | ISO 178 | 70.0 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 52.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 22 % |
| Flexural modulus | 23°C | ISO 178 | 2300 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 1 |
| High arc combustion index (HAI) | 0.75mm | UL 746 | PLC 0 |
| 1.5mm | UL 746 | PLC 0 | |
| 3.0mm | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 4 |
| 1.5mm | UL 746 | PLC 4 | |
| 3.0mm | UL 746 | PLC 3 | |
| Volume resistivity | 0.750mm | IEC 60093 | 1E+11 ohms·cm |
| dielectric strength | 1.00mm | IEC 60243 | 12 kV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 75.0 °C |
| 3.0mm | UL 746 | 75.0 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 63.0 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| 线性热膨胀系数 | MD：23to55°C,2.00mm | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD：23to55°C,2.00mm | ISO 11359-2 | 1.4E-04 cm/cm/°C | |
| RTI Elec | 0.75mm | UL 746 | 130 °C |
| 1.5mm | UL 746 | 130 °C | |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 0.75mm | UL 746 | 75.0 °C |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/B | 185 °C |
| RTI Str | 0.75mm | UL 746 | 115 °C |
| 1.5mm | UL 746 | 115 °C | |
| 3.0mm | UL 746 | 115 °C |