PA66 Staramide AST44 EUROSTAR FRANCE

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	-20°C	ISO 180/1A	65	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	55	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	>100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	>100	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	80	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	65	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	80	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning rate	2.00mm	FMVSS302	15	mm/min
UL flame retardant rating	0.75mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield	ISO 527-2/50	50.0	MPa
Tensile modulus		ISO 527-2/1	1900	MPa
elongation	Yield3	ASTM D638	4.6	%
elongation	elongation	Break	ISO 527-2/50	>100	%
bending strength		ISO 178	72.0	MPa
Bending modulus		ISO 178	1900	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature	--	ISO 306/B50	192	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	72.0	°C
Vicat softening temperature	--	ISO 306/B120	190	°C
Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	1.2E-04	cm/cm/°C
RTI Elec		UL 746	65.0	°C
RTI Imp		UL 746	65.0	°C
RTI		UL 746	65.0	°C
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	220	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.5	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	5.5	%
Shrinkage rate	MD	Internal Method	1.9to2.1	%
density		ISO 1183	1.07	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	50Hz	IEC 60250	6.7E-03
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Surface resistivity		IEC 60093	>1.0E+16	ohms
Relative permittivity	1MHz	IEC 60250	2.70
	Relative permittivity	60Hz	IEC 60250	2.90
	Relative permittivity	Relative permittivity	50Hz	IEC 60250	2.90
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16	kV/mm
Dissipation factor	60Hz	IEC 60250	6.7E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.015
Compared to the anti leakage trace index		IEC 60112	PLC 1
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Sale	ISO 2039-2	112

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.