EVA ELEVATE™ EF529 USA Huamei Chemistry

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
turbidity	31.8μm,Blown Film	ASTM D1003	3.6 %
gloss	45°,31.8μm,Blown Film	ASTM D2457	82

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Melting temperature		ASTM D3418	85.0 °C
Vicat softening temperature		ASTM D1525	67.0 °C

Physical properties	روش آزمون	نتیجه آزمون
Vinyl acetate content		18.5 wt%
melt mass-flow rate	ASTM D1238	2.5 g/10min
density	ASTM D1505	0.940 g/cm³

film	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	MD:Break,32μm,Blown Film	ASTM D882	600 %
tensile strength	TD:Break,32μm,Blown Film	ASTM D882	24.1 MPa
tensile strength	tensile strength	MD:Break,32μm,Blown Film	ASTM D882	24.8 MPa
Secant modulus	1%Secant,TD:32μm,Blown Film	ASTM D882	50.3 MPa
Secant modulus	Secant modulus	1%Secant,MD:32μm,Blown Film	ASTM D882	42.1 MPa
film thickness			32 µm
Dart impact	32μm,Blown Film	ASTM D1709	290 g
elongation	TD:Break,32μm,Blown Film	ASTM D882	800 %

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
Cast Film Melt Temperature			<204 °C
BlownFilmMeltTemperature			<177 °C