XLPE Polidan® EC/110
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Changes in mechanical properties after hot air aging test | 拉伸强度变化 | IEC 60811 | 15 % |
| 拉伸伸长率变化 | IEC 60811 | -8 % | |
| thermosetting | 200°C，冷却后最大永久伸长率 | IEC 60811 | 0.0 % |
| 200℃下，负荷断裂伸长率 | IEC 60811 | <70 % | |
| Hot air contraction | 130°C | IEC 60811 | <4.0 % |
| Volume resistivity | 20°C | IEC 60502 | 4.1E+15 ohms·cm |
| density | ASTM D792 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | 内部方法 | 0.70 g/10min |
| Water absorption rate | 24小时:100°C | IEC 60811 | <0.500 mg/cm² |
| 336小时:85°C | IEC 60811 | <0.500 mg/cm² | |
| Shore hardness | 邵氏D | ISO 868 | 51 |
| tensile strength | Break | IEC 60811 | 21.6 MPa |
| Bending test variation - in air, | 150°C | IEC 60811 | 无开裂 |
| Volume resistivity | 90°C | IEC 60502 | 2.7E+15 ohms·cm |
| dielectric strength | ASTM D149 | 34 kV/mm | |
| dielectric constant | 1kHz | ASTM D150 | 2.30 |
| Dissipation Factor | 1kHz | ASTM D150 | 6E-04 |
| dielectric constant | 20°C | IEC 60502 | 15000 Mohms·km |
| 90°C | IEC 60502 | 10000 Mohms·km | |
| elongation | Break | IEC 60811 | 500 % |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.