ABS Terluran® GP-22 BK BASF BELGIUM

ویژگی‌ها:
جریان بالا
سختی بالا
مقاومت متوسط
کاربردها:
پوسته
پوشش تلویزیون
لوازم خانگی کوچک
مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	平衡,23°C,50%RH	ISO 62	0.22 %
density		ASTM D792	1.04 g/cm³
density	density		ISO 1183	1.04 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.5 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	19 g/10min
Melt volume flow rate	230°C/3.8kg	ASTM D1238	4.80 cm3/10min
Melt volume flow rate	Melt volume flow rate	220°C/10.0kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	MD	ASTM D955	0.40-0.70 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40-0.70 %
Water absorption rate	饱和,23°C	ASTM D570	1.0 %
Water absorption rate	Water absorption rate	饱和,23°C	ISO 62	1.0 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R级	ASTM D785	103
ball-indentation hardness		ISO 2039-1	97.0 Mpa

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Yellowness Index		DIN 6167	13 YI

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus		ISO 527-2	2300 Mpa
tensile strength	屈服,23°C	ASTM D638	45.0 Mpa
tensile strength	tensile strength	屈服,23°C	ISO 527-2	45.0 Mpa
Tensile strain	屈服,23°C	ISO 527-2	2.6 %
elongation	断裂	ASTM D638	2.6 %
Nominal tensile fracture strain	23°C	ISO 527-2	10 %
Flexural modulus		ASTM D790	2300 Mpa
bending strength		ASTM D790	65.0 Mpa
bending strength	bending strength		ISO 178	65.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	22 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	180 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	59 J/m
	Impact strength of cantilever beam gap	-18°C	ASTM D256	100 J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	300 J/m
			Impact strength of cantilever beam gap	-30°C	ISO 180/A	8.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	26 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		IEC 60093	1E+13 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	1E+15 ohms·cm
dielectric constant	1.00mm,1MHz	ASTM D150	2.80
relative permittivity	100Hz	IEC 60250	2.90
relative permittivity	relative permittivity	1MHz	IEC 60250	2.80
Dissipation Factor	100Hz	IEC 60250	4.8E-03
Dissipation Factor	Dissipation Factor	1MHz	IEC 60250	7.9E-03

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5to1.1E-4 cm/cm/°C
thermal conductivity		DIN 52612	0.17 W/m/K
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	90.6 °C
	Heat distortion temperature	0.45MPa,退火，HDT	ASTM D648	104 °C
		Heat distortion temperature	0.45MPa,Annealed，HDT	ISO 75-2/B	99.0 °C
			Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	77.8 °C
				Heat distortion temperature	1.8MPa,退火，HDT	ASTM D648	98.9 °C
				Heat distortion temperature	Heat distortion temperature	1.8MPa,退火，HDT	ISO 75-2/A	94.0 °C
vicat	--	ISO 306/A50	105 °C
vicat	vicat	--	ISO 306/B50	96.0 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.