EHMWPE Quadrant EPP TIVAR® 1000 UV Stabilized Natural
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| compressive strength | 10%应变,23°C | ASTM D695 | 20.7 MPa |
| density | ASTM D792 | 0.930 g/cm³ | |
| Water absorption rate | 24hr | ASTM D570 | <0.010 % |
| shear strength | ASTM D732 | 33.1 MPa | |
| Water absorption rate | Saturation | ASTM D570 | <0.010 % |
| Shore hardness | 邵氏D | ASTM D2240 | 66 |
| Tensile modulus | ASTM D638 | 689 MPa | |
| coefficient of friction | Steel - Static | 内部方法 | 0.12 |
| Impact strength of cantilever beam gap | ASTM D256A | 无断裂 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 46.7 °C |
| Maximum operating temperature LongTerm, Air | 82 °C | ||
| Crystallization peak temperature | DSC | ASTM D3418 | 135 °C |
| Linear coefficient of thermal expansion | MD2：-40到149°C | ASTME831 | 3.6E-04 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.41 W/m/K | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| tensile strength | Ultimate | ASTM D638 | 40.0 MPa |
| elongation | Break | ASTM D638 | 300 % |
| Flexural modulus | ASTM D790 | 758 MPa | |
| bending strength | Yield | ASTM D790 | 24.1 MPa |
| Compression Modulus | ASTM D695 | 0.552 MPa | |
| dielectric strength | ASTM D149 | 91 kV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 2.30 |
| Dissipation Factor | 1MHz | ASTM D150 | 5E-04 |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| limiting pv value | 内部方法 | 0.0701 MPa·m/s |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.