POM 500P（粉） POM vs. - Plastic Material Properties Comparison Chart at Plas.com

Supplementary Information	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
EmissionofOrganicCompounds		VDA277	10.0 µgC/g
Odor		VDA270	3.50
Emission		VDA275	<2.00 mg/kg
mechanical properties	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
bending strength	3.5%Strain	ISO 178	85.0 Mpa
Tensile modulus		ISO 527-2	3350 Mpa
Tensile strain	Yield	ISO 527-2	13 %
Nominal tensile fracture strain		ISO 527-2	27 %
tensile strength	Yield	ISO 527-2	73.5 Mpa
Bending modulus		ISO 178	3150 Mpa
thermal performance	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
		MD：--	ISO 11359-2	1E-04 cm/cm/°C
		TD：AnnealingTime-Optional	ISO 11359-2	30.0 min/mm
		TD：AnnealingTemperature	ISO 11359-2	160 °C
		TD：--	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	159 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	103 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
Melting temperature		ISO 11357-3	178 °C
Physical properties	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
MediumDensity			1.20 g/cm³
Shrinkage rate	MD	ISO 294-4	2.0 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.90 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
melt mass-flow rate		ISO 1133	14 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.8 %
flammability	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
Burning rate	1.00mm	ISO 3795	<100 mm/min
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	3.5E-04 g
Electrical performance	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
Dissipation factor	100Hz	IEC 60250	5E-04
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	5.5E-03
Relative permittivity	100Hz	IEC 60250	3.90
Surface resistivity		IEC 60093	>1.0E+15 ohms
Relative permittivity	1MHz	IEC 60250	3.80
Dielectric strength		IEC 60243-1	43 KV/mm
impact performance	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	250 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	230 kJ/m²
hardness	شرایط آزمون	روش آزمون	DUPONT USA/500P（粉）
Rockwell hardness	M-Sale	ISO 2039-2	93
Rockwell hardness		R-Sale	ISO 2039-2	121