PC/ABS MC1300-100 PC/ABS vs. - Plastic Material Properties Comparison Chart at Plas.com

injection	شرایط آزمون	روش آزمون	SABIC INNOVATIVE NANSHA/MC1300-100
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			255 to 290 °C
Spray nozzle temperature			260 to 290 °C
Screw speed			40 to 70 rpm
Mold temperature			75 to 100 °C
Exhaust hole depth			0.038 to 0.076 mm
Processing (melt) temperature			260 to 290 °C
drying temperature			100 to 105 °C
Suggested injection volume			30 to 80 %
Temperature in the middle of the barrel			255 to 290 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			250 to 280 °C
mechanical properties	شرایط آزمون	روش آزمون	SABIC INNOVATIVE NANSHA/MC1300-100
elongation	Break	ASTM D638	150 %
Bending modulus	50.0 mm Span	ASTM D790	2060 Mpa
Tensile modulus		ASTM D638	2130 Mpa
tensile strength	Break	ASTM D638	44.0 Mpa
tensile strength		Yield	ASTM D638	50.0 Mpa
elongation	Yield	ASTM D638	8.6 %
bending strength	Yield, 50.0 mm Span	ASTM D790	72.0 Mpa
Physical properties	شرایط آزمون	روش آزمون	SABIC INNOVATIVE NANSHA/MC1300-100
Water absorption rate	24 hr	ASTM D570	0.10 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14 g/10 min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80 %
thermal performance	شرایط آزمون	روش آزمون	SABIC INNOVATIVE NANSHA/MC1300-100
thermal conductivity		ASTM C177	0.20 W/m/K
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
Vicat softening temperature		ASTM D15255	111 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	98.0 °C
Hot deformation temperature		0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
impact performance	شرایط آزمون	روش آزمون	SABIC INNOVATIVE NANSHA/MC1300-100
Dart impact	23°C, Total Energy	ASTM D3763	40.0 J
Dart impact		-30°C, Total Energy	ASTM D3763	33.0 J