GPPS PG-33 GPPS vs. - Plastic Material Properties Comparison Chart at Plas.com

mechanical properties	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
bending strength		ISO 178	75.0 Mpa
elongation	Break	ASTM D638	2.0 %
bending strength		ASTM D790	65.6 Mpa
tensile strength	Break	ISO 527-2/50	48.0 Mpa
Tensile strain	Break	ISO 527-2/50	2.0 %
tensile strength	Break	ASTM D638	45.0 Mpa
Bending modulus		ASTM D790	3030 Mpa
Bending modulus			ISO 178	3100 Mpa
thermal performance	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
Vicat softening temperature	--	ISO 306/B50	90.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	5.0E-5to8.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/A50	94.0 °C
Vicat softening temperature			ASTM D15257	94.0 °C
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	87.0 °C
		1.8MPa,Annealed	ISO 75-2/A	87.0 °C
		1.8MPa,Unannealed	ASTM D648	79.0 °C
		1.8MPa,Unannealed	ISO 75-2/A	76.0 °C
impact performance	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
Charpy Notched Impact Strength	23°C	ISO 179	2.7 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²
		23°C,6.40mm	ASTM D256	15 J/m
		23°C,3.20mm	ASTM D256	17 J/m
		-30°C	ISO 180/1A	1.8 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	1.8 kJ/m²
Physical properties	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	8.00 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	8.0 g/10min
density	23°C	ISO 1183	1.04 g/cm³
density		比重	ASTM D792	1.05 g/cm³
hardness	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
Rockwell hardness	M-Scale	ASTM D785	77
flammability	شرایط آزمون	روش آزمون	TAIWAN CHIMEI/PG-33
UL flame retardant rating	1.5mm	UL 94	HB

تماس با ما

دریافت اپلیکیشن