PA46 TE200F8 PA46 vs. - Plastic Material Properties Comparison Chart at Plas.com

mechanical properties	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
tensile strength	Break, 120°C	ISO 527-2	130 Mpa
		Break, 180°C	ISO 527-2	105 Mpa
		Break, 160°C	ISO 527-2	115 Mpa
Tensile strain	Break, 160°C	ISO 527-2	6.5 %
Bending modulus	--	ISO 178	11500 Mpa
Tensile strain	Break, 180°C	ISO 527-2	6.5 %
Tensile strain		Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	230 Mpa
Tensile modulus	--	ISO 527-2	13000 Mpa
		180°C	ISO 527-2	5700 Mpa
		200°C	ISO 527-2	5300 Mpa
Tensile strain	Break, 120°C	ISO 527-2	6.5 %
Tensile modulus	120°C	ISO 527-2	6900 Mpa
Bending modulus	160°C	ISO 178	5200 Mpa
Bending modulus		120°C	ISO 178	5800 Mpa
Tensile modulus	160°C	ISO 527-2	6100 Mpa
Tensile strain	Break, 200°C	ISO 527-2	6.5 %
tensile strength	Break, 200°C	ISO 527-2	100 Mpa
thermal performance	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	5.0E-5 cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Thermal Index - 5000 hr		IEC 60216	159 °C
Melting temperature		ISO 11357-3	295 °C
Physical properties	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
density		ISO 1183	1.51 g/cm³
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.2 %
Shrinkage rate	Flow	ISO 294-4	0.50 %
Shrinkage rate		横向Flow	ISO 294-4	1.1 %
impact performance	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	12 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	75 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14 kJ/m²
Electrical performance	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
Compared to the anti leakage trace index		IEC 60112	PLC 1
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Relative permittivity	100 Hz	IEC 60250	4.40
Relative permittivity		1 MHz	IEC 60250	4.00
Dielectric strength		IEC 60243-1	35 KV/mm
flammability	شرایط آزمون	روش آزمون	DSM HOLAND/TE200F8
Flammability level		UL 94	HB