PA6T TKR4355G10 PA6T vs. - Plastic Material Properties Comparison Chart at Plas.com

thermal performance	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Temperature index - at 50% loss of tensile strength	--6	IEC 60216	145 °C
Temperature index - at 50% loss of tensile strength		--5	IEC 60216	170 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	245 °C
specific heat			1000 J/kg/°C
Maximum operating temperature	短周期操作		260 °C
thermal conductivity		DIN 52612	0.32 W/m/K
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	1.8E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : 23 to 55°C	ISO 11359-2	5.0E-5 到 6.0E-5 cm/cm/°C
Melting temperature		ISO 11357-3	285 °C
injection	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Residence Time			< 5.0 min
Temperature at the front of the material cylinder			320 °C
Spray nozzle temperature			320 °C
Screw speed			< 18 m/min
Mold temperature			80 to 120 °C
Processing (melt) temperature			310 to 330 °C
drying temperature			110 °C
Temperature in the middle of the barrel			310 °C
drying time			8.0 hr
Suggested maximum moisture content			0.15 %
Hopper temperature			80 °C
Temperature at the rear of the barrel			300 °C
Physical properties	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Mold Shrinkage - Constrained			0.29 %
Stickiness	96% H2SO4	ISO 307	135 cm³/g
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.40 to 0.80 %
Shrinkage rate	Flow	ISO 294-4	0.20 %
Water absorption rate	Saturation, 23°C	ISO 62	3.5 to 4.5 %
Shrinkage rate	横向Flow	ISO 294-4	0.66 %
Apparent density			0.70 g/cm³
mechanical properties	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Tensile strain	Break	ISO 527-2	2.4 %
tensile strength	Break	ISO 527-2	240 Mpa
Tensile modulus		ISO 527-2	17000 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
impact performance	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	85 kJ/m²
flammability	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Polymer Abbreviation			PA6T/6-GF50
Flammability level		UL 94	HB
Electrical performance	شرایط آزمون	روش آزمون	BASF GERMANY/TKR4355G10
Volume resistivity		IEC 60093	1.0E+17 ohms·cm
Dissipation factor	1 MHz	IEC 60250	0.020
Relative permittivity	1 MHz	IEC 60250	4.70
Surface resistivity		IEC 60093	-- ohms
Dielectric strength		IEC 60243-1	33 KV/mm

تماس با ما

دریافت اپلیکیشن