PA66 HTN53G50LWSF BK083 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

impact performance	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
Charpy Notched Impact Strength	Dry	ISO 179/1eA	15 kJ/m²
Impact strength of cantilever beam gap	Dry，-40℃	ISO 180/1A	15 kJ/m²
Impact strength of cantilever beam gap		Dry，23℃	ISO 180/1A	236 °C
Charpy Notched Impact Strength	Dry，23℃	ISO 179/1eA	95 kJ/m²
combustion performance	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
UL flame retardant rating	HB	UL 94	1.5 mm
FMVSS combustion rate		FMVSS 302	B -
Burning rate	1mm	ISO 3795	25 mm/min
Limiting Oxygen Index (LOI)		ISO 4589-1/-2	27 %
mechanical properties	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
Elongation at Break	Conditio	ISO 527-1/-2	3.2 %
Poisson's ratio	Dry	ISO 527-1/-2	14
Elongation at Break	Dry	ISO 527-1/-2	2.8 %
Bending modulus	Dry	ISO 178	15000 Mpa
tensile strength	Conditione，Break	ISO 527-1/-2	215 Mpa
tensile strength		Dry，Break	ISO 527-1/-2	250 Mpa
Tensile modulus	Conditio	ISO 527-1/-2	16300 Mpa
Tensile modulus		Dry	ISO 527-1/-2	16500 Mpa
thermal properties	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
Linear coefficient of thermal expansion	Across Flow	ISO 11359-1/-2	55 E-6/K
RTI Imp		UL 746B	65 °C
Melting temperature		ISO 11357-1/-3	260 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-1/-2	14 E-6/K
		-40-23°C，Flow	ISO 11359-1/-2	17 E-6/K
		-40-23°C，Across Flow	ISO 11359-1/-2	55 E-6/K
RTI Elec		UL 746B	65 °C
Electrical Property	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
Compared to the Leakage Traceability Index (CTI)		IEC 60112	600 -
Volume resistivity		IEC 60093	10000000000000 Ohm-m
Physical properties	شرایط آزمون	روش آزمون	DUPONT SHENZHEN/HTN53G50LWSF BK083
Shrinkage rate	Dry	ISO 294-4	0.4 %
Shrinkage rate		Dry，Flow	ISO 294-4	0.2 %