PBT 5010N6 PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

injection	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
Drying time - vacuum dryer			5.0 to 8.0 hr
Injection speed			中等偏快
Temperature at the front of the material cylinder			250 °C
Spray nozzle temperature			245 °C
Screw speed			80 to 120 rpm
Mold temperature			60 to 80 °C
Injection pressure			20.0 to 150 Mpa
Temperature in the middle of the barrel			240 °C
Drying Temperature - Vacuum Drying Machine			120 °C
Temperature at the rear of the barrel			235 °C
mechanical properties	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
bending strength		ISO 178	90.0 Mpa
Tensile modulus		ISO 527-2/1	2800 Mpa
tensile strength	Yield	ISO 527-2/50	55.0 Mpa
Tensile strain	Break	ISO 527-2/50	50 %
Bending modulus		ISO 178	2600 Mpa
Tensile strain	Yield	ISO 527-2/50	4.3 %
flammability	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
UL flame retardant rating	1.6 mm	UL 94	V-0
		0.71 mm	UL 94	V-0
		3.2 mm	UL 94	V-0
Physical properties	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
Shrinkage rate	横向Flow : 2.00 mm	Internal Method	1.8 %
Water absorption rate	Saturation, 23°C	ISO 62	0.080 %
Shrinkage rate	Flow : 2.00 mm	Internal Method	1.9 %
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	20.0 cm3/10min
thermal performance	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
Hot deformation temperature	1.8 MPa, Annealed	ISO 75-2/A	77.0 °C
Linear coefficient of thermal expansion	Flow : -30 to 35°C	ISO 11359-2	8.0E-5 cm/cm/°C
RTI Elec	0.71 mm	UL 746	140 °C
Hot deformation temperature	0.45 MPa, Annealed	ISO 75-2/B	165 °C
Linear coefficient of thermal expansion	Across Flow : 35 to 120°C	ISO 11359-2	1.5E-4 cm/cm/°C
		Across Flow : -30 to 120°C	ISO 11359-2	1.2E-4 cm/cm/°C
		Flow : -30 to 120°C	ISO 11359-2	1.2E-4 cm/cm/°C
RTI Imp	0.71 mm	UL 746	120 °C
RTI	0.71 mm	UL 746	140 °C
Linear coefficient of thermal expansion	Flow : 35 to 120°C	ISO 11359-2	1.4E-4 cm/cm/°C
Melting temperature		ISO 11357-3	224 °C
Linear coefficient of thermal expansion	Across Flow : -30 to 35°C	ISO 11359-2	8.8E-5 cm/cm/°C
Electrical performance	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
Compared to the anti leakage trace index		UL 746	PLC 1
Dielectric strength	1.00 mm	IEC 60243-1	21 KV/mm
Volume resistivity		IEC 60093	1.0E+16 ohms·cm
Dissipation factor	1 MHz	IEC 60250	0.020
Dielectric strength	2.00 mm	IEC 60243-1	18 KV/mm
Surface resistivity		IEC 60093	1.0E+15 ohms
Dielectric constant	1 MHz	IEC 60250	3.20
impact performance	شرایط آزمون	روش آزمون	JAPAN POLYPLASTIC/5010N6
Impact strength of simply supported beam without notch	23°C	ISO 179	120 kJ/m²