PC XHT1141-BK1C141 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

injection	شرایط آزمون	روش آزمون	SABIC INNOVATIVE US/XHT1141-BK1C141
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			290 to 335 °C
Spray nozzle temperature			285 to 330 °C
Screw speed			40 to 90 rpm
Mold temperature			85 to 130 °C
Exhaust hole depth			0.025 to 0.080 mm
Processing (melt) temperature			290 to 335 °C
drying temperature			125 °C
Suggested injection volume			40 to 60 %
Temperature in the middle of the barrel			280 to 325 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			270 to 315 °C
mechanical properties	شرایط آزمون	روش آزمون	SABIC INNOVATIVE US/XHT1141-BK1C141
bending strength		ISO 178	100 Mpa
Tensile modulus		ISO 527-2/1	2400 Mpa
tensile strength	Break	ISO 527-2/50	60.0 Mpa
tensile strength		Yield	ISO 527-2/50	65.0 Mpa
Tensile strain	Break	ISO 527-2/50	80 %
Bending modulus		ISO 178	2400 Mpa
Tensile strain	Yield	ISO 527-2/50	6.5 %
thermal performance	شرایط آزمون	روش آزمون	SABIC INNOVATIVE US/XHT1141-BK1C141
Vicat softening temperature	--	ISO 306/B50	150 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	132 °C
Hot deformation temperature		0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Bf	144 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : -40 to 40°C	ISO 11359-2	7.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	152 °C
impact performance	شرایط آزمون	روش آزمون	SABIC INNOVATIVE US/XHT1141-BK1C141
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	16 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂
Physical properties	شرایط آزمون	روش آزمون	SABIC INNOVATIVE US/XHT1141-BK1C141
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.30 %
Water absorption rate		Saturation, 23°C	ISO 62	0.30 %
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	70.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.90 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	16.0 cm3/10min