PA66 CM3001G50 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

mechanical properties	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Friction coefficient - vs. Metal		Suzuki Method	0.15
Tensile strain	Break, -40°C	ISO 527-2	2.0 %
shear strength	23°C	ASTM D732	95.0 Mpa
Compressive stress	80°C	ISO 604	110 Mpa
tensile strength	23°C	ISO 527-2	190 Mpa
bending strength	23°C	ISO 178	290 Mpa
Compressive stress	23°C	ISO 604	180 Mpa
tensile strength	80°C	ISO 527-2	120 Mpa
Bending modulus	80°C	ISO 178	5800 Mpa
bending strength	80°C	ISO 178	190 Mpa
Bending modulus	23°C	ISO 178	9500 Mpa
Tensile strain	Break, 23°C	ISO 527-2	2.5 %
tensile strength	-40°C	ISO 527-2	235 Mpa
Tensile strain	Break, 80°C	ISO 527-2	5.0 %
Compressive stress	-40°C	ISO 604	250 Mpa
Taber abraser	1000 Cycles	ISO 9352	0.400 mg
bending strength	-40°C	ISO 178	325 Mpa
Bending modulus	-40°C	ISO 178	11600 Mpa
thermal performance	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C
specific heat			1800 J/kg/°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5 cm/cm/°C
Melting temperature		DSC	265 °C
thermal conductivity			0.40 W/m/K
Electrical performance	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Arc resistance		UL 746	114 sec
Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
Dielectric constant	23°C, 1 kHz	IEC 60250	4.40
Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
Volume resistivity		IEC 60093	1.0E+13 ohms·cm
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
Dielectric strength		IEC 60243-1	20 KV/mm
Dielectric constant	23°C, 1 MHz	IEC 60250	3.90
Dielectric constant		23°C, 50 Hz	IEC 60250	4.60
impact performance	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Charpy Notched Impact Strength	23°C	ISO 179	13 kJ/m²
Charpy Notched Impact Strength		-40°C	ISO 179	10 kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179	60 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	65 kJ/m²
Physical properties	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Water absorption rate	24 hr, 23°C	ISO 62	0.60 %
Water absorption rate		Saturation, 23°C	ISO 62	5.5 %
Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.50 %
Shrinkage rate		横向Flow : 3.00 mm	Internal Method	0.60 - 0.90 %
density	23°C	ISO 1183	1.37 g/cm³
flammability	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
UL flame retardant rating	0.79 mm	UL 94	HB
hardness	شرایط آزمون	روش آزمون	TORAY JAPAN/CM3001G50
Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121
		R -Sale, 80°C	ISO 2039-2	24
		M -Sale, 23°C	ISO 2039-2	97