TPV 3170B DSM HOLAND

برگه‌های اطلاعات پلاستیک

Supplementary Information	شرایط آزمون	روش آزمون	DSM HOLAND/3170B
ApparentShearViscosity-Capillary,@206/s	200°C	ISO 11443	290 Pa·s
ApparentShearViscosity-Capillary,@206/s		200°C	ASTM D3835	290 Pa·s

hardness	شرایط آزمون	روش آزمون	DSM HOLAND/3170B
Shore hardness	ShoreA,5Sec,挤塑	ISO 868	71
		ShoreA,5Sec,Injection	ISO 868	75
		ShoreA,5Sec,挤塑	ASTM D2240	71
		ShoreA,5Sec,Injection	ASTM D2240	75

thermal performance	روش آزمون	DSM HOLAND/3170B
RTI Elec	UL 746	50.0 °C
RTI Imp	UL 746	50.0 °C
RTI Str	UL 746	50.0 °C

flammability	شرایط آزمون	روش آزمون	DSM HOLAND/3170B
UL flame retardant rating	1.5mm	UL 94	HB

aging	شرایط آزمون	روش آزمون	DSM HOLAND/3170B
Change rate of hardness (Shore) in the air	ShoreA,150°C,168hr	ASTM D573	3.0
		ShoreA,150°C,168hr	ISO 188	3.0
		ShoreA,135°C,1000hr	ISO 188	-1.0
		ShoreA,135°C,1000hr	ASTM D573	-1.0
Change rate of tensile strength in air	100%Strain135°C,1000hr，Across Flow	ISO 188	10 %
		150°C,168hr，Across Flow	ASTM D573	-4.0 %
		100%Strain150°C,168hr，Across Flow	ISO 188	5.0 %
		100%Strain,135°C,1000hr，Across Flow	ASTM D573	10 %
		150°C,168hr，Across Flow	ISO 188	-4.0 %
		135°C,1000hr，Across Flow	ASTM D573	-8.0 %
		135°C,1000hr，Across Flow	ISO 188	-8.0 %
		100%Strain,150°C,168hr，Across Flow	ASTM D573	5.0 %
Change rate of ultimate elongation in air	150°C,168hr，Across Flow	ASTM D573	-14 %
Change rate of ultimate elongation in air		135°C,1000hr，Across Flow	ASTM D573	-13 %
Tensile stress change rate	150°C,168hr，Break	ISO 188	-14 %
Tensile stress change rate		135°C,1000hr，Break	ISO 188	-13 %
Volume change	125°C,70hr,在IRM903油中	ISO 1817	120 %
Volume change		125°C,70hr,在IRM903油中	ASTM D471	120 %

elastomer	شرایط آزمون	روش آزمون	DSM HOLAND/3170B
elongation	Break	ISO 37	670 %
		Flow:Break	ASTM D412	300 %
		Break	ASTM D412	670 %
		Flow:Break	ISO 37	300 %
Permanent compression deformation	70°C,22hr	ISO 815	43 %
		70°C,22hr	ASTM D395	43 %
		125°C,70hr	ASTM D395	63 %
		125°C,70hr	ISO 815	63 %
		23°C,22hr	ISO 815	25 %
		23°C,22hr	ASTM D395	25 %
tear strength	横向Flow	ISO 34-1	42 kN/m
tear strength		横向Flow	ASTM D624	42.0 kN/m
tensile strength	横向Flow:100%Strain	ISO 37	3.30 Mpa
		Flow:Break	ISO 37	6.70 Mpa
		Flow:100%Strain	ASTM D412	5.10 Mpa
		Break	ASTM D412	7.72 Mpa
		Flow:100%Strain	ISO 37	5.10 Mpa
		Break	ISO 37	7.70 Mpa
		Flow:Break	ASTM D412	6.70 Mpa
		横向Flow:100%Strain	ASTM D412	3.30 Mpa