PPS A673MT B PPS vs. - Plastic Material Properties Comparison Chart at Plas.com

Electrical performance	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Volume resistivity		IEC 60093	1E+16 ohms·cm
Dielectric constant	23°C,1MHz	IEC 60250	3.80
Dielectric strength		IEC 60243-1	26 KV/mm
mechanical properties	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
tensile strength	Yield,23°C	ISO 527-2	150 Mpa
Bending modulus	23°C	ISO 178	10000 Mpa
shear strength	23°C	JISK7214	68.0 Mpa
Taber abraser	1000Cycles	ISO 9352	50.0 mg
Friction coefficient			0.25
bending strength	23°C	ISO 178	225 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.5 %
Physical properties	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
Water absorption rate	23°C,24hr	ISO 62	0.020 %
Shrinkage rate	TD:3.00mm2	Internal Method	0.85 %
Shrinkage rate		MD:3.00mm4	Internal Method	0.20 %
flammability	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
UL flame retardant rating		UL 94	V-0
impact performance	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
Impact strength of simply supported beam without notch	23°C	ISO 179	60 kJ/m²
thermal performance	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
Linear coefficient of thermal expansion	TD	ISO 11359-2	3.3E-05 cm/cm/°C
Linear coefficient of thermal expansion		MD	ISO 11359-2	2.2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	255 °C
Melting temperature		ISO 11357-3	278 °C
Supplementary Information	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
BarFlowLength	320°C,1.00mm	Internal Method	150 mm
hardness	شرایط آزمون	روش آزمون	TORAY JAPAN/A673MT B
Rockwell hardness	R-Scale	ISO 2039-2	114