مقایسه مواد

اطلاعات محصول

نام محصول

نام برند

کاربردها

ویژگی‌ها

گواهی‌نامه‌ها

PETG 0601 EASTMAN USA

لوازم ورزشی,بسته بندی

شفافیت بالا,مقاومت بالا

برگه‌های اطلاعات پلاستیک

hardness	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Rockwell hardness	R-Sale,23°C	ISO 2039-2	109
Rockwell hardness		R-Scale,23°C	ASTM D785	106

thermal performance	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Glass transition temperature		DSC	80.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	64.0 °C
Hot deformation temperature		0.45MPa,Unannealed	ASTM D648	70.0 °C
Linear coefficient of thermal expansion	MD：-30to40°C	ASTM D696	5.1E-05 cm/cm/°C
specific heat	60°C	DSC	1300 J/kg/°C
		150°C	DSC	1880 J/kg/°C
		250°C	DSC	2050 J/kg/°C
		200°C	DSC	1970 J/kg/°C
		100°C	DSC	1760 J/kg/°C
thermal conductivity	23°C	ASTMC177	0.21 W/m/K
Vicat softening temperature		ASTM D1525	85.0 °C

film	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Carbon dioxide transmittance	23°C	ASTM D1434	49 cm³·mm/m²/atm/24hr
Dart impact	-18°C	ASTM D1709A	500 g
Dart impact		23°C	ASTM D1709A	400 g
Elmendorf tear strength	MD	ASTM D1922	1400 g
Elmendorf tear strength		TD	ASTM D1922	1700 g
elongation	MD:Yield	ASTM D882	4.0 %
		TD:Yield	ASTM D882	4.0 %
		MD:Break	ASTM D882	400 %
		TD:Break	ASTM D882	400 %
film thickness			250 µm
Oxygen permeability	23°C	ASTM D3985	10 cm³·mm/m²/atm/24hr
Secant modulus	MD	ASTM D882	1900 Mpa
Secant modulus		TD	ASTM D882	1900 Mpa
Tear resistance of pants type	MD	ISO 6383-1	36.0 N/mm
Tear resistance of pants type		TD	ISO 6383-1	36.0 N/mm
tear strength	M.D.:23°C	ASTM D1938	36 kN/m
tear strength		T.D.:23°C	ASTM D1938	36 kN/m
tensile strength	TD:Break	ASTM D882	55.0 Mpa
		MD:Break	ASTM D882	59.0 Mpa
		MD:Yield	ASTM D882	52.0 Mpa
		TD:Yield	ASTM D882	52.0 Mpa
Water vapor permeability	38°C,100%RH	ASTMF1249	7.0 g/m²/24hr

mechanical properties	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Bending modulus	23°C	ISO 178	2000 Mpa
Bending modulus		23°C	ASTM D790	2100 Mpa
bending strength	23°C	ISO 178	68.0 Mpa
bending strength		Yield,23°C	ASTM D790	70.0 Mpa
elongation	Break,23°C	ISO 527-2	100 %
elongation		Break,23°C	ASTM D638	130 %
tear strength	M.D.:23°C	-	93 N
tear strength		T.D.:23°C	-	93 N
Tensile modulus	23°C	ASTMD638	2100 Mpa
tensile strength	Yield,23°C	ASTMD638	50.0 Mpa
tensile strength		Break,23°C	ASTMD638	28.0 Mpa

Electrical performance	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Arc resistance		ASTM D495	158 sec
Dielectric constant	23°C,1kHz	ASTM D150	2.60
Dielectric constant		23°C,1MHz	ASTM D150	2.40
Dielectric strength	23°C	ASTM D149	16 KV/mm
Dissipation factor	23°C,1kHz	ASTM D150	5E-03
Dissipation factor		23°C,1MHz	ASTM D150	0.020
Surface resistivity		ASTM D257	1E+16 ohms
Volume resistivity	23°C	ASTM D257	1E+15 ohms·cm

Physical properties	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Intrinsic viscosity	Film:23°C	Internal Method	0.70
Intrinsic viscosity		Pellets:23°C	Internal Method	0.75
Water absorption rate	23°C,24hr	ASTMD570	0.13 %

impact performance	شرایط آزمون	روش آزمون	EASTMAN USA/0601
Dart impact	-40°C,2.50mm,EnergyatPeakLoad	ASTM D3763	41.0 J
		23°C,2.50mm,EnergyatPeakLoad	ASTM D3763	28.0 J
		-40°C,3.20mm,能量to力量峰值8,9	ISO 6603-2	36.0 J
		23°C,3.20mm,EnergyatPeakLoad	ASTM D3763	33.0 J
		23°C,3.20mm,能量to力量峰值8,9	ISO 6603-2	44.0 J
		-40°C,3.20mm,EnergyatPeakLoad	ASTM D3763	50.0 J
		-40°C,2.50mm,能量to力量峰值8,9	ISO 6603-2	35.0 J
		23°C,2.50mm,能量to力量峰值8,9	ISO 6603-2	40.0 J
Suspended wall beam without notch impact strength	-30°C7	ISO 180/1U	无断裂
		-40°C,3.20mm	ASTM D4812	无断裂
		-20°C,3.20mm	ASTM D4812	无断裂
		-30°C,3.20mm	ASTM D4812	无断裂
		23°C,3.20mm	ASTM D4812	无断裂
		-40°C7	ISO 180/1U	无断裂
		-20°C7	ISO 180/1U	无断裂
		23°C7	ISO 180/1U	无断裂

optical performance	شرایط آزمون	روش آزمون	EASTMAN USA/0601
gloss	45°	ASTM D2457	108
transmissivity	Total	ASTM D1003	91.0 %
transmissivity		常规	ASTM D1003	89.0 %
transparency		ASTM D1746	85.0
turbidity		ASTM D1003	0.80 %