ABS 5000 ABS vs. - Plastic Material Properties Comparison Chart at Plas.com

Physical properties	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
density		ASTM D792	1.04 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.0 g/10min
Water absorption rate	24hr	ASTM D570	<0.30 %
Shrinkage rate	MD	ASTM D955	<0.40 %
melt mass-flow rate	220°C/10.0kg	ASTM D1238	20 g/10min
impact performance	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	200 J/m
Impact strength of cantilever beam gap		23°C,6.35mm	ASTM D256	180 J/m
thermal performance	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	83.0 °C
RTI Imp	1.6mm	UL 746	60.0 °C
Vicat softening temperature		ASTM D15254	103 °C
RTI Elec	1.6mm	UL 746	60.0 °C
RTI Str	1.6mm	UL 746	60.0 °C
mechanical properties	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
tensile strength	Yield,23°C,3.18mm	ASTM D638	42.1 Mpa
elongation	Break,23°C,3.18mm	ASTM D638	30 %
tensile strength	Break,23°C,3.18mm	ASTM D638	35.2 Mpa
Bending modulus	23°C	ASTM D790	2550 Mpa
bending strength	Yield,23°C	ASTM D790	73.5 Mpa
Electrical performance	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
Hot wire ignition	1.57mm	UL 746	PLC 3 sec
High arc combustion index	1.57mm	UL 746	PLC 0
flammability	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
UL flame retardant rating	1.6mm	UL 94	HB
hardness	شرایط آزمون	روش آزمون	TAIDA TAIWAN/5000
Rockwell hardness	R-Sale,23°C	ASTM D785	115