برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr ASTM D-570 0.20 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D-638 3000 Mpa tensile strength Yield ASTM D-638 42.7 Mpa tensile strength Break ASTM D-638 39.3 Mpa elongation at yield ASTM D-638 2.2 % Elongation at Break ASTM D-638 8.6 % Bending modulus ASTM D-790 2820 Mpa bending strength ASTM D-790 75.8 Mpa Impact strength of cantilever beam gap 3.18mm ASTM D-256 58.7 J/m Suspended wall beam without notch impact strength 3.18mm ASTM D-256 286 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.80MPa,Unannealed ASTM D-648 87.8 °C Linear coefficient of thermal expansion Flow ASTM E-831 0.000079 cm/cm/℃ Linear coefficient of thermal expansion Transverse ASTM E-831 0.000096 cm/cm/℃ Hot deformation temperature 0.45MPa,Unannealed ASTM D-648 97.2 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Flow,24hr ASTM D-955 18 % Shrinkage rate Across,Flow,24hr ASTM D-955 27 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D-4496 1.0-1.0E+5 ohms Volume resistivity ASTM D-257 1E+06 ohm.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.