برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break Break点 ASTM D-638 50 % tensile strength 屈伏点 ASTM D-638 59 Mpa Impact strength of cantilever beam gap 23℃ ASTM D-256 427 J/m Tensile modulus ASTM D-638 2687 Mpa Rockwell hardness ASTM D-785 120 R bending strength ASTM D-790 96 Mpa Bending modulus ASTM D-790 2687 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Long term use temperature 无冲击 UL -746B 60 °C Vicat softening temperature ASTM D-1525 90 °C UL flame retardant rating UL -94 1.5 mm Linear coefficient of thermal expansion E-831 - 1/℃ Hot deformation temperature 0.45Mpa ASTM D-648 - °C UL flame retardant rating UL -94 V-0 Hot deformation temperature 1.8Mpa ASTM D-648 80 °C Long term use temperature 含冲击 UL -746B 60 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3.2mm ASTM D-955 4-6 E-3 Water absorption rate ASTM D-570 0.1 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant 1MHz ASTM D-150 - Surface resistivity ASTM D257 1E+14 ohm-cm Dissipation factor 1MHz ASTM D-150 - Volume resistivity ASTM D-257 1E+17 ohm-cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.