برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 2 g/min Water absorption rate 浸水24hrs后増重 ASTM D-570 0.3 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap Lzod 研磨Notched ASTM D-256 1.5(14.7) kgf-cm/cm(J/m) Impact strength of cantilever beam gap 落锤(15.2*15.2*0.3cm)重1.4kg 半径0.64cm ASTM D-256 14(1.6) kg-cm(J) Rockwell hardness ASTM D-758(M级) 99 tensile strength 初级Strain速率0.1cm/cm/min ASTM D-638 767(75) Kgf/cm Bending modulus ASTM D-790 34000 Kgf/cm bending strength 横夸比=16 ASTM D-790 1460(143) Kgf/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D-648 103 °C Vicat softening temperature Unannealed ASTM D-1525 113 °C Temperature range for use 与残余应力大小有关 85-105 Vicat softening temperature 50℃/hr,1kg ASTM D-1525 235 F
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Transmittance rate ASTM D-1003 93 % Refractive index ASTM D-542 1.49 Flame retardant performance UL 94 HB CLASS density ASTM D-792 1.18 Shrinkage rate ASTM D-955 0.4-0.8 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.