Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
78 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
21 kJ/m²
Impact strength of cantilever beam gap
-40°C
ISO 180/1A
14 kJ/m²
tensile strength
23°C
ISO 527-2
145 Mpa
Elongation at Break
23°C
ISO 527-2
3.5 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
220 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
205 °C
Vicat softening temperature
Melting Temperature
ISO 11357-3
220 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
(23°C,24hr)
ISO 62
0.90 %
Water absorption rate
(23°C,50RH)
ISO 62
1.50 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+10 Ω.cm
Dielectric strength
IEC 60243-1
11 KV/mm
Dielectric constant
23°C
IEC 60250
3.60 100HZ
Dielectric constant
23°C
IEC 60250
3.40 1MHz
Dissipation factor
23°C
IEC 60250
0.010 100HZ
Dissipation factor
23°C
IEC 60250
0.010 1MHz
Dissipation factor
相对漏电起痕指数
IEC 60112
600 V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 0.80mm
UL flame retardant rating
UL -94
HB 1.50mm
UL flame retardant rating
UL -94
HB 3.00mm
Ignition temperature of heating wire
3.00mm
IEC 60695-2-12
750 °C
Relative temperature of heating wire
3.00mm
IEC 60695-2-13
960 °C