برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 高钢性.耐热 purpose 自动车部件
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 湿 2.1 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 干(湿) ASTM D-256 49(59) J/m tensile strength 干(湿) ASTM D-638 108(79) Mpa Rockwell hardness 干(湿) ASTM D-785 94(71) M Scale Rockwell hardness 干(湿) ASTM D-785 120(-) R scale flexural coefficient 干(湿) ASTM D-790 4.9(2.5) GPa Elongation at Break 干(湿) ASTM D-638 2.5(8) % bending strength 干(湿) ASTM D-790 167(108) Mpa Charpy Notched Impact Strength ASTM D256/ISO 179 49 kg·cm/cm(J/M)ft·lb/in Rockwell hardness ASTM D785 M94 Bending modulus ASTM D790/ISO 178 4900 kg·cm/cm(J/M)ft·lb/in bending strength ASTM D790/ISO 178 167 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 干 UL 94 HB Linear coefficient of thermal expansion 干 ASTM D-696 4 ×10-5/K Hot deformation temperature 1.82MPa,干 ASTM D-648 240 °C Hot deformation temperature 0.46MPa,干 ASTM D-648 258 °C Combustibility (rate) UL 94 HB Hot deformation temperature HDT ASTM D648/ISO 75 240 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 4 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 干 旭化成方法 0.7/1.2 % Wear factor 湿 ASTM D-1044 9 ×10-6kg/1000times density ASTM D792/ISO 1183 1.25 Water absorption rate ASTM D570/ISO 62 2.1 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.