برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D-790 1960 Mpa bending strength ASTM D-790 69 Mpa tensile strength Yield ASTM D-638 49 Mpa tensile strength Yield ASTM D-638 500 kg/cm Impact strength of cantilever beam gap ASTM D-256 5 kg.cm/cm Bending modulus ASTM D-790 20000 kg/cm tensile strength Yield ASTM D-638 7100 psi Impact strength of cantilever beam gap ASTM D-256 0.9 ft.lb/in elongation Break ASTM D-638 10 % bending strength ASTM D-790 700 Kg./cm Bending modulus ASTM D-790 290 psi bending strength ASTM D-790 10000 psi Impact strength of cantilever beam gap ASTM D-256 50 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45Mpa ASTM D-648 - °C Hot deformation temperature 0.45Mpa ASTM D-648 - °F Hot deformation temperature 1.82Mpa ASTM D-648 140 °C Hot deformation temperature 1.82Mpa ASTM D-648 285 °F
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 0.99 Shrinkage rate ASTM D-955 0.4-0.6 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.