Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate			优等品｜3.01-5.00 g/10min
	melt mass-flow rate			一等品｜1.01-3.00 g/10min
	melt mass-flow rate	melt mass-flow rate			合格品｜0.50-1.00 g/10min

Other performance	شرایط آزمون	روش آزمون	نتیجه آزمون
block ratio			优等品｜30/70 S/B
	block ratio			一等品｜30/70 S/B
	block ratio	block ratio			合格品｜30/70 S/B
compression set			优等品｜≤20 %
	compression set			一等品｜≤30 %
	compression set	compression set			合格品｜≤40 %
Volatile compounds			优等品｜≤0.50 %
	Volatile compounds			一等品｜≤0.70 %
	Volatile compounds	Volatile compounds			合格品｜≤1.00 %
ash content			优等品｜≤0.20 %
	ash content			一等品｜≤0.20 %
	ash content	ash content			合格品｜≤0.20 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile stress	300%伸长率		一等品｜≥2.0 Mpa
Tensile stress	Tensile stress	300%伸长率		合格品｜≥1.7 Mpa
elongation at break			优等品｜≥815 %
	elongation at break			一等品｜≥750 %
	elongation at break	elongation at break			合格品｜≥700 %
Shore hardness			优等品｜75±7
	Shore hardness			一等品｜75±7
	Shore hardness	Shore hardness			合格品｜75±7
tensile strength			优等品｜≥18.0 Mpa
	tensile strength			一等品｜≥15.0 Mpa
	tensile strength	tensile strength			合格品｜≥12.0 Mpa
Tensile stress	300%伸长率		优等品｜≥2.5 Mpa