Impact strength of simply supported beam without notch
低温-30℃
ISO 179 1eU
12 J/cm
Charpy Notched Impact Strength
低温-30℃
ISO 179 1eA
0.6 J/cm
Impact strength of simply supported beam without notch
23℃
ISO 179 1eU
12.0 J/cm
Bending modulus
ISO 178
2700 Mpa
Tensile modulus
1mm/min
ISO 527 part 1/2
2800 Mpa
elongation
伸长率
ISO 527 part 1/2
9.0 %
Elongation at Break
50mm/min
ISO 527 part 1/2
20 %
tensile strength
50mm/min,Yield
ISO 527 part 1/2
65 Mpa
Ball Pressure Test
30sec数值
ISO 2039 part 1
140 Mpa
Tensile modulus
ASTM D638/ISO 527
392000 kg/cm²(MPa)[Lb/in²]
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Vicat softening temperature
VST/B/50
ISO 306
150 °C
Hot deformation temperature
1.8MPa
ISO 75 part 1/2
100 °C
Melting temperature
DSC,10 K/min
ISO 3146 method C1b
166 °C
Linear coefficient of thermal expansion
23-55℃ Longitudinal
ISO 11359 part 1/2
110 µm/m-℃
Vicat softening temperature
ASTM D1525/ISO R306
302 ℃(℉)
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ASTM D792/ISO 1183
1.41
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric strength
IEC 60243 part 1
35 KV/mm
Dielectric constant
低频100 Hz
IEC 60250
4.20
Dielectric constant
1 MHz
IEC 60250
4.20
Dissipation factor
低频100 Hz
IEC 60250
0.0025
Dissipation factor
IEC 60250
0.008 1 MHz
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.