برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation 3.2mmt ASTM D-638 2.2 % tensile strength ASTM D-256 2300 Mpa tensile strength 3.2mmt ASTM D-638 210 Mpa Tensile modulus 3.2mmt ASTM D-638 17600 Mpa Impact strength of cantilever beam gap 带Notched ASTM D-256 137 J/m shear strength ASTM D-732 84 Mpa bending strength 3.2mmt ASTM D-790 253 Mpa Rockwell hardness ASTM D-785 84 R Bending modulus 3.2mmt ASTM D-790 14700 Mpa Charpy Notched Impact Strength ASTM D256/ISO 179 35 kg·cm/cm(J/M)ft·lb/in tensile strength ASTM D638/ISO 527 210 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 15000 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 270 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.82MPa ASTM D-648 230 °C Combustibility (rate) UL 94 V-0
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Poisson's ratio 0.49 Water absorption rate 23℃蘸涂,Equilibrium状态 ASTM D-570 0.05 % Water absorption rate 23℃ 50%相对温度Equilibrium状态 ASTM D-570 0.05 % density ASTM D792/ISO 1183 1.61 Water absorption rate ASTM D570/ISO 62 0.02 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric constant ASTM D150/IEC 60250 4.1 Dielectric constant ASTM D150/IEC 60250 3.7 Arc resistance ASTM D495/IEC 60112 137 Volume resistivity ASTM D257/IEC 60093 3 x 10^16 Ω.cm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.