برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity 6350μm ASTM D1003 6.0 %
impact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C ASTM D1822 1020 kJ/m² Impact strength of cantilever beam gap -40°C ASTM D1822 1010 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear resistance NBS指数 ASTM D1630 610 Bending modulus 23°C ASTM D790 330 Mpa Bending modulus -20°C ASTM D790 731 Mpa Tensile strain Break,23°C ISO 527-2 290 % elongation Break,23°C ASTM D638 290 % tensile strength Break,23°C ISO 527-2 24.8 Mpa tensile strength Break,23°C ASTM D638 24.8 Mpa tensile strength Yield,23°C,CompressionMolded ASTM D638 13.8 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Brittle temperature ASTM D746 -105 °C FreezingPoint -- ISO 3146 46 °C FreezingPoint -- ASTM D3418 46 °C Melting temperature ISO 3146 86.0 °C Melting temperature ASTM D3418 86.0 °C Vicat softening temperature ISO 306 62.0 °C Vicat softening temperature ASTM D1525 62.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون IonType Zinc melt mass-flow rate 190°C/2.16kg ISO 1133 0.70 g/10min melt mass-flow rate 190°C/2.16kg ASTM D1238 0.70 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreD ISO 868 64 Shore hardness ShoreD ASTM D2240 64