برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength Injection ASTM D790 89.6 Mpa bending strength Compression Molded ASTM D790 56.5 Mpa Bending modulus Injection ASTM D790 3190 Mpa Bending modulus Compression Molded ASTM D790 3100 Mpa elongation Break,Injection ASTM D638 2.0 % elongation Break,Compression Molded ASTM D638 1.0 % tensile strength Ultimate,Injection ASTM D638 46.9 Mpa tensile strength Ultimate,Compression Molded ASTM D638 40.0 Mpa tensile strength Yield,Injection ASTM D638 46.9 Mpa tensile strength Yield,Compression Molded ASTM D638 40.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 105 °C Hot deformation temperature 1.8MPa,Annealed ASTM D648 102 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 82.8 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D955 0.40-0.70 % melt mass-flow rate 200°C/5.0kg ASTM D1238 8.5 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.