برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1.00mm ISO 3795 <100 mm/min FMVSS flammability FMVSS302 B
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength ISO 178 130 Mpa Tensile modulus ISO 527-2 7000 Mpa tensile strength Break ISO 527-2 80.0 Mpa Tensile strain Break ISO 527-2 1.3 % Bending modulus ISO 178 6100 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 200 °C Melting temperature ISO 11357-3 310 °C Linear coefficient of thermal expansion MD:-- ISO 11359-2 4.5E-05 cm/cm/°C Linear coefficient of thermal expansion MD:-40to23°C ISO 11359-2 4.3E-05 cm/cm/°C Linear coefficient of thermal expansion MD:55to160°C ISO 11359-2 5.1E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-- ISO 11359-2 6E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-40to23°C ISO 11359-2 5.3E-05 cm/cm/°C Linear coefficient of thermal expansion TD:55to160°C ISO 11359-2 8.6E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate TD ISO 294-4 1.0 % Shrinkage rate MD ISO 294-4 0.60 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.