برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D-790 710 kg/cm2 Bending modulus ASTM D-790 24000 kg/cm2 tensile strength ASTM D-638 430 kg/cm2 Rockwell hardness ASTM D-785 100 R-Scale Elongation at Break ASTM D-638 18 % Impact strength of cantilever beam gap Notched1/4" ASTM D-256 18 kgcm/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Burning rate 1/16" IEC 707 FV-0 mm/min Vicat softening temperature 1.000g ASTM D-1525 85 °C Burning rate 1/16" UL -94 V-0 Hot deformation temperature Unannealed18.5kg/cm2,1/2" ASTM D-648 76 °C Burning rate 1/8" UL -94 V-0
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.004-0.007 mm/mm melt mass-flow rate 220℃/10kg ASTM D-1238 60 g/10min density ASTM D-792 1.20
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Arc resistance ASTM D-495 PLC_7 Hot wire ignition UL -746A PLC 5 Compared to the anti leakage trace index UL -746A PLC 5 High voltage arc tracing rate UL -746A PLC 2 High arc combustion index UL -746A PLC 0
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.