Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
65 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
68 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.8mm
UL 94
V-0
Burning wire flammability index
1.0mm
IEC 60695-2-12
960 °C
Burning wire flammability index
2.0mm
IEC 60695-2-12
960 °C
Hot filament ignition temperature
1.0mm
IEC 60695-2-13
725 °C
Hot filament ignition temperature
2.0mm
IEC 60695-2-13
725 °C
Burning rate
FMVSS302
0.0 mm/min
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2/1A/1
7900 Mpa
tensile strength
Break
ISO 527-2/1A/5
120 Mpa
Tensile strain
Break
ISO 527-2/1A/5
3.3 %
Bending modulus
ISO 178
6900 Mpa
bending strength
ISO 178
185 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/Af
230 °C
Vicat softening temperature
ISO 306/B50
240 °C
Melting temperature
ISO 11357
260 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
Saturation,23°C,2.00mm
ISO 62
5.5 %
Water absorption rate
Equilibrium,23°C,2.00mm,50%RH
ISO 62
1.2 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
1E+12 ohms
Volume resistivity
IEC 60093
1E+15 ohms·cm
Compared to the anti leakage trace index
IEC 60112
PLC 1
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.