Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
90 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
22 kJ/m²
Impact strength of cantilever beam gap
-30°C
ISO 180/1A
7 kJ/m²
Elongation at Break
23°C
ISO 527-2
2.4 %
Tensile modulus
23°C
ISO 527-2
2300 Mpa
bending strength
23°C
ISO 178
65 Mpa
Charpy Notched Impact Strength
23°C
ISO 179/1eA
19 kJ/m²
Charpy Notched Impact Strength
-30°C
ISO 179/1eA
7 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
130 kJ/m²
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaAnnealed
ISO 75-2/B
95 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/A
92 °C
Vicat softening temperature
ISO 306/A50
102 °C
Vicat softening temperature
ISO 306/B50
95 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
8E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion
导热系数
DIN 52612
0.17 W/m/K
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD2.0mm
ISO 294-4
0.55 %
Water absorption rate
(23°C,24hr)
ISO 62
0.95 %
Water absorption rate
(23°C,50RH)
ISO 62
0.24 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+15 Ω.cm
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Ball Pressure Test
ISO 2039-1
99 Mpa
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 0.80mm
UL flame retardant rating
UL -94
HB 1.50mm
UL flame retardant rating
UL -94
HB 3.00mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.