Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
90 kJ/m²
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
80 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
15 kJ/m²
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
250 °C
Vicat softening temperature
ISO 306/B50
255 °C
Vicat softening temperature
玻璃转化温度
ISO 11357-2
80 °C
Vicat softening temperature
Melting Temperature
ISO 11357-3
260 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.7E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
8.5E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD2.0mm
ISO 294-4
0.30 %
Shrinkage rate
TD2.0mm
ISO 294-4
0.70 %
Water absorption rate
(23°C,24hr,2.00mm)
ISO 62
5.50 %
Water absorption rate
(23°C,50RH,2.00mm)
ISO 62
1.70 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
>1.0E+15 Ω.cm
Dielectric strength
IEC 60243-1
36 KV/mm
Dissipation factor
相对漏电起痕指数
IEC 60112
400 V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL -94
HB 0.71mm
UL flame retardant rating
UL -94
HB 1.50mm
Extreme Oxygen Index
ISO 4589-2
24 %