برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 V-1 UL flame retardant rating 3.0mm UL 94 V-0 UL flame retardant rating 2.5mm UL 94 5VA
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Poisson's ratio ASTM D638 0.38 Friction coefficient Steel - Static ASTM D1894 0.42 Friction coefficient Itself - Static ASTM D1894 0.44 Taber abraser 1000Cycles,1000g,CS-17Wheel ASTM D1044 35.0 mg tensile strength Break ASTM D638 127 Mpa elongation Yield ASTM D638 1.5 % Bending modulus 100mmSpan ASTM D790 9650 Mpa bending strength Yield,100mmSpan ASTM D790 159 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI UL 746 50.0 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 124 °C Linear coefficient of thermal expansion MD:-40to95°C ASTME831 2.2E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-40to95°C ASTME831 3.2E-05 cm/cm/°C RTI Elec UL 746 50.0 °C RTI Imp UL 746 50.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:3.20mm Internal Method 0.15 % Shrinkage rate TD:3.20mm Internal Method 0.25 % Water absorption rate 24hr ASTM D570 0.060 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1E+17 ohms Volume resistivity ASTM D257 1E+17 ohms·cm Dielectric strength 1.60mm,inAir ASTM D149 25 KV/mm Arc resistance ASTM D495 PLC 5 Compared to the anti leakage trace index CTI UL 746 PLC 4 High arc combustion index HAI UL 746 PLC 4 High voltage arc tracing rate HVTR UL 746 PLC 4 Hot wire ignition HWI UL 746 PLC 0
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 90