برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Suspended wall beam without notch impact strength 23°C ASTM D4812 无断裂
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break ASTM D638 53.0 Mpa elongation Break ASTM D638 53 % Bending modulus ASTM D790 2270 Mpa bending strength ASTM D790 81.0 Mpa Friction coefficient Dynamic ASTM D3702 0.28 Friction coefficient Static ASTM D3702 0.17 Wear factor ASTM D3702 2.0E+7 10^-8 mm³/N·m
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 120 °C drying time 4.0 hr Suggested maximum moisture content 0.020 % Temperature at the rear of the barrel 295 to 305 °C Temperature in the middle of the barrel 305 to 315 °C Temperature at the front of the material cylinder 310 to 320 °C Processing (melt) temperature 300 to 315 °C Mold temperature 80 to 110 °C Back pressure 0.200 to 0.300 Mpa Screw speed 30 to 60 rpm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm ASTM D648 128 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Flow : 24hr ASTM D955 0.70 - 0.90 % Shrinkage rate Across FlowFlow : 24hr ASTM D955 0.70 - 0.90 %