برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.75mm UL 94 HB UL flame retardant rating 3.0mm UL 94 HB
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 1.14 melt mass-flow rate ASTM D-1238 50 g/10min
elastomer شرایط آزمون روش آزمون نتیجه آزمون elongation Break ASTM D412 430 % tear strength ASTM D624 140 kN/m Permanent compression deformation 23°C,22hr ASTM D395B 30 % Permanent compression deformation 70°C,22hr ASTM D395B 45 % tensile strength 100%Strain ASTM D412 17.2 Mpa tensile strength 300%Strain ASTM D412 35.9 Mpa tensile strength ASTM D412 39.3 Mpa
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus Injection ASTM D412 51.7 Mpa Bending modulus Injection ASTM D790 52.4 Mpa Taber abraser ASTM D1044 55.0 mg Wear resistance DIN 53516 25 mm³ tensile strength Break ASTM D-412 48.3 Mpa elongation Break ASTM D-412 450 % tear strength ASTM D-624 140 kN/m Shore hardness shoreA ASTM D-648 95 Tensile modulus ASTM D-638 41.4 Mpa Tensile stress 100%伸长率 ASTM D-412 16.5 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Glass transition temperature Internal Method -28.0 °C Vicat softening temperature ASTM D1525 127 °C Vicat softening temperature Internal Method 89 °C Vicat softening temperature ASTM D-1525 116 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 210°C/10.0kg ASTM D1238 35to65 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreA ASTM D2240 95