برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield,5mm/min,23°C ASTM D638 46.0 Mpa tensile strength 5mm/min,23°C ASTM D638 47.0 Mpa Elongation at Break Yield,5mm/min,23°C ASTM D638 4.2 % Elongation at Break 5mm/min,23°C ASTM D638 100 % Tensile modulus 50mm/min,23°C ASTM D638 2480 Mpa bending strength Yield,1.3mm/min,23°C ASTM D790 80.0 Mpa bending strength 1.3mm/min,23°C ASTM D790 79.0 Mpa Bending modulus 1.3mm/min,23°C ASTM D790 2400 Mpa Impact strength of cantilever beam gap 23°C ASTM D256 600 J/m Impact strength of cantilever beam gap 悬壁梁Unnotched冲击强度 ASTM D4812 NB J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.80MPaUnannealed ASTM D648 108 °C Linear coefficient of thermal expansion MD ASTM D696 8.47E-05 cm/cm/°C Linear coefficient of thermal expansion TD ASTM D696 9.1E-05 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD3.20mm ASTM D995 0.60-0.65 % Shrinkage rate TD3.20mm ASTM D995 0.50-0.56 % Water absorption rate (23°C,24hr) ASTM D570 0.010 % Water absorption rate 吸湿性 ASTM D570 0.0200 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.