برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون bending strength ASTM D-1052 >8×10
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr ASTM D-570 1.5 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 10%伸长 ASTM D-638 10.5 Mpa Shore hardness ASTM D-2240 55 Elongation at Break Break ASTM D-638 31 Mpa Rubbing modulus 23℃ ASTM D-790 193 Mpa Impact strength of cantilever beam gap 23℃ ASTM D-256 不破裂 J/m Initial tear strength ASTM D-1004 123 kN/m Elongation at Break ASTM D-648 375 % tensile strength 5%伸长 ASTM D-638 6.0 Mpa Elongation at Break ASTM D412/ISO 527 31 % Elongation at Break ASTM D412/ISO 527 375 % Rockwell hardness ASTM D785 55 Bending modulus ASTM D790/ISO 178 193 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature ASTM D-3418 215 °C Vicat softening temperature ASTM D-1525 196 °C Hot deformation temperature @0.18Mpa ASTM D-648 51 °C Hot deformation temperature @0.5Mpa ASTM D-648 111 °C Melting temperature 215 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 196 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Taber abraser CS-17轮 ASTM D-1044 9 mg/1000rev Taber abraser H 18轮 ASTM D-1044 116 mg/1000rev melt mass-flow rate ASTM D-1238 10 g/10min density ASTM D955 1.22 % melt mass-flow rate ASTM D1238/ISO 1133 10 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.