برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون remarks 增强.纤维
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 3 % tensile strength ASTM D638/ISO 527 580 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 90 Bending modulus ASTM D790 ≥70000 kg/cm bending strength ASTM D790 1500-1900 kg/cm Impact strength of cantilever beam gap 切口1/4″ ASTM D256 7-11 kg-cm/cm Shore hardness ASTM D785 85-90 M-scale Elongation at Break ASTM D638 2.5-4.5 % tensile strength ASTM D638 950-1250 kg/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility (rate) UL 94 V-0 Melting temperature 225 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 36 mm/mm.℃ Hot deformation temperature 18.6kg/cm ASTM D648 195(210) °C Melting temperature DSC 225 °C Flame resistance 0.8mm UL 94 V-0 Linear coefficient of thermal expansion ASTM D696 3
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.54 Water absorption rate 24hr immersion ASTM D570 0.03 % Fiberglass content Ash 30 % Shrinkage rate Flow,- ASTM D955 0.1-0.4 % Shrinkage rate Across Flow,- ASTM D955 0.8-1.1 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Induced positive connection ASTM D150 0.01 60Hz Arc resistance ASTM D495 120 sec Volume resistivity ASTM D257 >10 Ω Volume resistivity ASTM D257 >10 Ω-cm Dielectric strength 2mm ASTM D149 >19 KV/mm Dielectric constant ASTM D150 3 60Hz
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.