Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
60 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Burning rate
1.00mm
ISO 3795
<100 mm/min
FMVSS flammability
FMVSS302
B
UL flame retardant rating
1.5mm
IEC 60695-11-10,-20
HB
UL flame retardant rating
0.8mm
IEC 60695-11-10,-20
HB
UL flame retardant rating
1.5mm
UL 94
HB
UL flame retardant rating
0.8mm
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
ISO 178
210 Mpa
Bending modulus
ISO 178
4900 Mpa
Tensile strain
Break
ISO 527-2
3.5 %
tensile strength
Break
ISO 527-2
125 Mpa
Tensile modulus
ISO 527-2
5500 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
TD:-40to23°C
ISO 11359-2
7E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:--
ISO 11359-2
7.3E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:-40to23°C
ISO 11359-2
3.4E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:--
ISO 11359-2
3.4E-05 cm/cm/°C
Melting temperature
ISO 11357-3
300 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
230 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
277 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD
ISO 294-4
0.40 %
Shrinkage rate
TD
ISO 294-4
0.70 %
density
ISO 1183
1.25 g/cm³
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
1E+15 ohms·cm