برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 抗静电 purpose 具有抗静电特性的部件
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638 51 Mpa Elongation at Break ASTM D638 15 % bending strength ASTM D790 87 Mpa Bending modulus ASTM D790 2780 Mpa Impact strength of cantilever beam gap ASTM D256 39 J/m Rockwell hardness ASTM D785 80 M Impact strength of cantilever beam gap ASTM D256/ISO 179 39 kg·cm/cm(J/M)ft·lb/in tensile strength ASTM D638/ISO 527 51 kg/cm²(MPa)[Lb/in²] elongation ASTM D638/ISO 527 15 % Rockwell hardness ASTM D785 80 Bending modulus ASTM D790/ISO 178 2780 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 87 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238 10 g/10min Linear coefficient of thermal expansion TMA法 10 Hot deformation temperature 1.82MPa ASTM D648 120 °C Hot deformation temperature 0.45MPa ASTM D648 162 °C UL flame retardant rating UL 94 HB Hot deformation temperature HDT ASTM D648/ISO 75 120 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 10 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate ASTM D570 0.2 % Shrinkage rate Flow 旭化成法 1.6-2.0 % Shrinkage rate Across Flow 旭化成法 1.6-2.0 % density ASTM D792/ISO 1183 1.41 Shrinkage rate ASTM D955 1.8 % melt mass-flow rate ASTM D1238/ISO 1133 10 g/10min Water absorption rate ASTM D570/ISO 62 0.2 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.