Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
340 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NoBreak
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
1.5mm
UL 94
HB
UL flame retardant rating
0.8mm
IEC 60695-11-10,-20
HB
UL flame retardant rating
1.5mm
IEC 60695-11-10,-20
HB
FMVSS flammability
FMVSS302
B
Burning rate
1.00mm
ISO 3795
25 mm/min
UL flame retardant rating
0.8mm
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
3150 Mpa
tensile strength
Yield
ISO 527-2
72.0 Mpa
Tensile strain
Yield
ISO 527-2
20 %
Nominal tensile fracture strain
ISO 527-2
40 %
Bending modulus
ISO 178
2950 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
165 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
98.0 °C
Melting temperature
ISO 11357-3
178 °C
AnnealingTemperature
160 °C
AnnealingTime-Optional
30.0 min/mm
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD
ISO 294-4
2.0 %
MediumDensity
1.16 g/cm³
SpecificHeatCapacity of Melt
3000 J/kg/°C
melt mass-flow rate
190°C/2.16kg
ISO 1133
2.4 g/10min
Shrinkage rate
TD
ISO 294-4
1.9 %
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Rockwell hardness
M-Sale
ISO 2039-2
94
Rockwell hardness
R-Sale
ISO 2039-2
122
Supplementary Information
شرایط آزمون
روش آزمون
نتیجه آزمون
Emission
VDA275
<8.00 mg/kg