'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT DURANEX® 2002 JAPAN POLYPLASTIC
345
- قیمت واحد:US$ ۳٬۷۵۰ /MT
- مشخصات بستهبندی:25 کیلوگرم / بسته
- جنس بستهبندی:کیسه کاغذی
- مقدار عرضه:50.1MT
- شرایط تحویل:FOB
- بندر بارگیری :Guangzhou port, China
- روشهای پرداخت قابل قبول:T/T
- حملونقل:برای جزئیات حمل و نقل با تامین کننده مذاکره کنید
توضیحات مواد
- ویژگیهای مواد:عقب نشینی｜انعطاف پذیری خوب｜تقویت فیبر شیشه ای｜مقاومت در برابر اصطکاک
- زمینههای کاربرد:زمینه برق｜حوزه الکترونیک
- رنگ:--
- درجه:درجه تزریق
برگه داده فنی
| impact performance | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 190 | kJ/m² |
| 23°C | ISO 179/1eU | 无断裂 | ||
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| UL flame retardant rating | UL 94 | HB | ||
| 0.710mm | UL 94 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 22 | % | |
| mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| bending strength | ASTM D790/ISO 178 | 85 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2540 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 51 | kg/cm²(MPa)[Lb/in²] | |
| Elongation at Break | ASTM D638/ISO 527 | >200 | % | |
| Charpy Notched Impact Strength | ISO 179/1eA | 3.2 | kJ/m² | |
| Bending modulus | ISO 178 | 3100 | Mpa | |
| bending strength | ISO 178 | 95 | Mpa | |
| tensile strength | ISO 527-1/-2 | 57 | Mpa | |
| bending strength | ISO 178 | 95.0 | Mpa | |
| Bending modulus | ISO 178 | 3100 | Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 12 | % | |
| tensile strength | ISO 527-2 | 57.0 | Mpa | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 34 | kg·cm/cm(J/M)ft·lb/in | |
| Bending modulus | 23°C | ISO 178 | 2500 | Mpa |
| bending strength | 23°C | ISO 178 | 80.0 | Mpa |
| ASTM D-790 | 85 | Mpa | ||
| Yield, 0 ° C | Yield,0°C | ASTM D638 | 75.8 | Mpa |
| Surrender, 23 ° C | ASTM D638 | 55.8 | Mpa | |
| Yield, 80 ° C | ASTM D638 | 24.8 | Mpa | |
| Yield, 121 ° C | ASTM D638 | 17.9 | Mpa | |
| yield | ISO 527-2/1A/50 | 60.0 | Mpa | |
| elongation | ASTM D-638 | >200 | % | |
| -40°C | -40℃ | ASTM D638 | 3100 | Mpa |
| 23°C | ASTM D638 | 3170 | Mpa | |
| 80°C | 80℃ | ASTM D638 | 469 | Mpa |
| 121°C | 121℃ | ASTM D638 | 296 | Mpa |
| Surrender- 40°C | ASTM D638 | 101 | Mpa | |
| crack | ISO 527-2/1A/50 | 35.0 | Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 34 | J/m | |
| Bending modulus | ASTM D-790 | 2540 | Mpa | |
| tensile strength | ASTM D-638 | 51 | Mpa | |
| Yield, 80 ° C | ASTM D638 | 17 | % | |
| Yield, 121 ° C | ASTM D638 | 23 | % | |
| yield | ISO 527-2/1A/50 | 4.0 | % | |
| 50% strain | 50%Strain | ISO 527-2/1A/50 | 30.0 | Mpa |
| Surrender- 40°C | ASTM D638 | 7.2 | % | |
| Yield, 0 ° C | Yield,0°C | ASTM D638 | 4.4 | % |
| Surrender, 23 ° C | ASTM D638 | 3.2 | % | |
| Fracture, 23 ° C | ASTM D638 | 200 | % | |
| crack | ISO 527-2/1A/50 | 220 | % | |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | >50 | % | |
| thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 70 | ℃（℉） |
| 1.8MPa,Unannealed | ISO 75-2/A | 80.0 | °C | |
| UL flame retardant rating | UL 94 | HB | ||
| Hot deformation temperature | 1.8Mpa | ISO 75-1/-2 | 80 | °C |
| Linear coefficient of thermal expansion | TD：23to55°C | Internal Method | 9E-05 | cm/cm/°C |
| MD：23to55°C | Internal Method | 9E-05 | cm/cm/°C | |
| 0.45MPa, unannealed | ASTM D648 | 160 | °C | |
| ISO 75-2/B | 150 | °C | ||
| 1.8MPa, unannealed | ASTMD648 | 55.0 | °C | |
| Hot deformation temperature | 1.82Mpa | ASTM D-648 | 70 | °C |
| UL flame retardant rating | UL 94 | HB | ||
| Glass transition temperature | ISO 11357-2 | 60.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 190 | °C | |
| Melting temperature | ISO 11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 | cm/cm/°C |
| TD | ISO 11359-2 | 1.4E-04 | cm/cm/°C | |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| density | ASTM D792/ISO 1183 | 792 | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 | % |
| melt mass-flow rate | ASTM D1238 | 20 | g/10min | |
| Melt Volume Flow Rate (MVR) | 250°C/2.16kg | ISO 1133 | 18.0 | cm3/10min |
| flow | ASTM D955 | 1.8to2.0 | % | |
| Vertical flow direction | ISO 294-4 | 1.8to2.0 | % | |
| Flow | ISO 294-4 | 1.8to2.0 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.19 | % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| Dielectric strength | 3.00mm | IEC 60243-1 | 17 | KV/mm |
| 1MHz | 1MHz | ASTM D150 | 3.20 | |
| 100Hz | 100Hz | IEC 60250 | 4.00 | |
| 1MHz | 1MHz | IEC 60250 | 3.50 | |
| Dissipation factor | 100Hz | IEC 60250 | 1.4E-03 | |
| 1MHz | IEC 60250 | 0.022 | ||
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| Surface resistivity | IEC 60093 | 1E+15 | ohms | |
| --1 | ASTM D149 | 17 | KV/mm | |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| Rockwell hardness | M-Scale | ISO 2039-2 | 85 | |
| M-Sale | ISO 2039-2 | 78 | ||
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون | واحد آزمایش |
| ColourNumber | EF2001/ED3002 |