برگه داده فنی مقایسهmachinability شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 机械方向 ASTM D-955 0.3 % Shrinkage rate Across Flow ASTM D-955 0.7 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation ASTM D-638 1.4 % tensile strength ASTM D-638 152(1550) MPa(KG/cm Rockwell hardness ASTM D-785 123 Rscal bending strength ASTM D-790 250(2550) MPa(KG/cm Tensile modulus ASTM D-790 17(1.7) Impact strength of cantilever beam gap Notched ASTM D-955 59(6) J/m(kg.cm/cm) Impact strength of cantilever beam gap Unnotched ASTM D-955 343(35) J/m(kg.cm/cm)
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion Tosoh Method 2.0 Hot deformation temperature 18.6kg/cm ASTM D-648 >260 °C Linear coefficient of thermal expansion 0.37(0.32) W/M.K(kcal/m.hr.℃)
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D-257 1×10 Ω.cm Dielectric constant 1MHz ASTM D-150 4.7 Dissipation factor 1MHz ASTM D-150 0.0015 Dielectric strength ASTM D-149 14 KV/mm
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.