برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 3.0mm UL 94 HB UL flame retardant rating 0.75mm UL 94 HB
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون density ISO 1183 1.15 g/cm³
elastomer شرایط آزمون روش آزمون نتیجه آزمون Permanent compression deformation 70°C,22hr ASTM D395B 45 % Permanent compression deformation 23°C,22hr ASTM D395B 30 % tear strength ASTM D624 140 kN/m elongation Break ASTM D412 430 % tensile strength ASTM D412 39.3 Mpa tensile strength 300%Strain ASTM D412 35.9 Mpa tensile strength 100%Strain ASTM D412 17.2 Mpa
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Wear resistance DIN 53516 25 mm³ Taber abraser ASTM D1044 55.0 mg Bending modulus Injection ASTM D790 52.4 Mpa Tensile modulus Injection ASTM D412 51.7 Mpa tensile strength 300%Strain ISO 37 18 Mpa tensile strength 100%Strain ISO 37 10 Mpa Tensile strain Break ISO 527-2 500 % tensile strength Break ISO 527-2 55 Mpa Shore hardness Shore A ISO 868 96 tear strength ISO 34-1 100 kN/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 127 °C Glass transition temperature Internal Method -28.0 °C Vicat softening temperature Internal Method 89 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 210°C/10.0kg ASTM D1238 10to30 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreA ASTM D2240 95
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.