برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 注射成型/家电配件.汽车配件.家用器具
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D-1238 80.0 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D-638 350 kg/cm Impact strength of cantilever beam gap Notched, -20℃ ASTM D-256 3.0 kg•cm/cm Impact strength of cantilever beam gap Notched, 23℃ ASTM D-256 6.0 kg•cm/cm Bending modulus ASTM D-790 18000 kg/cm Rockwell hardness ASTM D-785 105 R scale Bending modulus ASTM D790/ISO 178 18000 kg/cm²(MPa)[Lb/in²] tensile strength ASTM D638/ISO 527 330 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 <100 % Impact strength of cantilever beam gap ASTM D256/ISO 179 6 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D-648 135 °C Vicat softening temperature ASTM D-1525 155 °C Vicat softening temperature ASTM D1525/ISO R306 155 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 80 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.